Mechanical properties and microstructure of primary and secondary AA6063 aluminum alloy after extrusion and T5 heat treatment

M. Cabibbo;M. El Mehtedi
2015-01-01

Abstract

The mechanical properties of primary and secondary AA6063 aluminum alloy were investigated in tension on samples with different orientation (extrusion direction, ED and transverse direction, TD), after quenching in forced air and after artificial aging (T5) at 185 °C for 6 h. The microstructure of the samples was analyzed using both light optical microscopy and scanning electron microscopy on the surface of the extrudate. The strength values after artificial aging are higher than the strength after quenching in forced air due to the precipitation hardening. The tensile properties show a slight anisotropy between ED and TD. The optical microscopy investigation carried out on the extruded billet after forced air quenching shows a fully recrystallized equiaxed grains. Artificial aging improves the strength and hardness due to the precipitation of Mg2Si observed by scanning electron microscopy (SEM)
2015
Inglese
MATERIALS TODAY: PROCEEDINGS
2, Part A
10
4890
4897
8
WOS:000369732400023
2-s2.0-84963538064
http://www.sciencedirect.com/science/article/pii/S2214785315008652
Esperti anonimi
internazionale
scientifica
Aluminium alloy; Hot extrusion; Aging; SEM; Tensile test; Microstructure
sì
Aydi, L.; Khlif, M.; Bradai, C.; Spigarelli, S.; Cabibbo, M.; El Mehtedi, M.
1.1 Articolo in rivista
info:eu-repo/semantics/article
1 Contributo su Rivista::1.1 Articolo in rivista
262
6
reserved
File in questo prodotto:
File Dimensione Formato  
1-s2.0-S2214785315008652-main.pdf

Solo gestori archivio

Descrizione: articolo
Tipologia: versione editoriale
Dimensione 1.2 MB
Formato Adobe PDF
  Visualizza/Apri   Richiedi una copia
1.2 MB Adobe PDF   Visualizza/Apri   Richiedi una copia

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Questionario e social

Condividi su:
Impostazioni cookie