Preliminary Results on Corrosion Rate in Carbonated LC3 Concrete
Bernhard ElsenerSupervision
;
2020-01-01
Abstract
The new blended cement, LC3, can reduce by up to a 30% of the CO2 emissions per ton of cement, including calcined clay and limestone as main components. However, the low level of clinker content concern about carbonation-induced corrosion of the reinforcing steel. The aim of this project is to measure the corrosion rate and understand the corrosion mechanism of reinforcing steel in concrete made with LC3 cement. The samples were cast in molds specifically designs in order to minimize the carbonation time and the moisture equilibration time. There is a finer porosity for LC3 cement and the porosity decrease when the carbonation takes place due to the transformation of the portlandite into calcite. However, when the clinker substitution is higher, the total porosity increase, but there is a coarsening porosity for blended systems after carbonation because the C-S-H are converted into calcite with a smaller volume. In all LC3 samples, the corrosion rate is higher compared with OPC cement, but there are differences regarding the induced carbonation and natural carbonation especially for LC3 samples with a more tortuous pore system than OPC assuring the high resistance to the carbonation.File | Dimensione | Formato | |
---|---|---|---|
Cabrera2020_Chapter_PreliminaryResultsOnCorrosionR.pdf Solo gestori archivio
Tipologia: versione editoriale
Dimensione 1.09 MB
Formato Adobe PDF
|
1.09 MB | Adobe PDF | Visualizza/Apri Richiedi una copia |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.